Testing Methods (COPONYL)

  • L-55E:Coronate L-55E (by Tosoh Corporation)
  • HX:Coronate HX (by Tosoh Corporation)
  • T-C:TETRAD-C (by Mitsubishi Gas Chemical Company)
  • N-2128:Metal Chelate Cross-linker
  • N-2235:Epoxy type Cross-linker
Photo Initiator
  • I-184:Irgacure 184 (by BASF Japan Ltd.)
  • I-500:Irgacure 500 (by BASF Japan .Ltd)
Substrate PET film (25µm)
Adhesive Thickness 25μm
Drying 100℃ × 2 min
Aging 40℃ × 3 days
UV Irradiation

80W/cm (High-pressure marcury lamp), 13cmH × 6.5m/min

Adherend Polished SUS 304
Others (Details in grade lists)
Adhesion 180°peeling (peeling speed : 300mm/min, 23℃×50%RH)
2kg roller× two times forwards and backwards Measured at 30 minutes after attachment
Holding Power Attachment area 25mm×25mm, 2kg roller× two times forwards and backwards 40℃ and 80℃× 1kg load × 24 hours
  • 【Result】
    • ◎No-creep
    • ○ Creep less than 2mm (after 24 hr)
    • △ Fallen within 24 hours
    • × Fallen within 1 hours/li>
Ball Tack J.Dow Method ∠30° 23℃×50%RH
Optical Properties
(Total Light Transmittance, Haze)

Data of adhesive layer
*Alkali-free glasses are attached on both sides

(Alkali-free glass Total light transparency : 92.8%, Haze : 0.02%)

Total light transparency, Haze : Tested with haze mater compliant to JIS K 7361-1

Relative Permitivity PET(50µm) / Adhesive / PET(50µm)

This site has been created based on Nippon Gohsei's technical knowledge, but does not necessarily guarantee performance in all applications. Similarly, figures contained herein are representative values, and not guaranteed values. Please use our products after fully examining their applicability, or contact us should you have any questions.

Top Page (COPONYL)

NOTE: COPONYL is a trademark of The Nippon Synthetic Chemical Industry Co., Ltd. (NIPPON GOHSEI).


Feel free to contact NIPPON GOHSEI for technical inquires and ordering or to request catalogs, pricing estimates, etc.


Page Top